SIFAT MEKANIS KOMPOSIT MATRIKS ALUMINIUM BERPENGUAT ABU JERAMI DENGAN METODE METALURGI SERBUK

A A ALIT TRIADI, S SUGIMAN, L.R. KALBI

Abstract


The powder metallurgy method is one method for making metal matrix composite products. This method provides researchers with material engineering.This study aims to determine how the effect of variations in mixing time and sintering holding time affects the hardness and compressive strength of composites made of aluminum powder and straw ash. The composition of this composite is 90%wt Aluminum and 10%wt straw ash. Preparation of specimens using powder metallurgy method. Mixing time variations were applied for 120, 150 and 180 minutes with the dry mixing method. Variation of sintering holding time was applied for 60, 120 and 180 minutes at 550°C.The mechanical test carried out are hardness test and compression test. The results showed that the optimum hardness value was found in the specimens with a mixing time of 150 minutes and sintering holding time of 180 minutes with an average hardness of 96 HRF. The optimum compressive strength is found in specimens with a mixing time of 150 minutes and sintering holding time of 120 minutes with an average compressive strength of 101.28 MPa. It can be concluded that mixing time and sintering holding time affect the hardness and compressive strength of the metal matrix composite.


Keywords


Powder Metallurgy; Hardness; Compressive strength; Aluminum; Straw ash

Full Text:

PDF

References


Anonim. (2006). Annual Book of ASTM Standards. International Standard Worldwide

El-Sayed, (2006). Physical and chemical property of rice straw ash and its effect on the cement paste produced from different cemen types, Jurusan Teknik Sipil Universitas Minofiya Egypt.

Malasyi, S. (2014) Analisis pengaruh penggunaan abu jerami terhadap kuat tekan beton. Teras Jurnal, Vol.4, No.2. Jurusan Teknik Sipil, Fakultas Teknik, Universitas Malikussaleh

Muzayyanah, N. (2021). Pemanfaatan limbah abu aluminium sebagai substitusi semen dalam pembuatan paving block. Universitas Islam Indonesia.

Polong, F. (2019). Pengaruh Tekanan Kompaksi Komposit Aluminium/Abu Jerami Terhadap Kekerasan. Universitas Tadulako.

Rifai, M. (2020). Pengaruh Temperatur Sintering Terhadap Keausan Dan Struktur Mikro Komposit Aluminium/Abu Jerami. Universitas Tadulako.

Ruzuqi, R. (2020). Tensile Strength Analysis Of Polymer Composite Materials Fiber Reinforced In The Fiber Boat Application. Journal of Research and Opinion, 7(8), 2763-2769.

Sukma, H., Prasetyani, R., Rahmalina, D., & Imanuddin, R. (2015). Peran Penguat Partikel Alumina Dan Silikon Karbida Terhadap Kekerasan Material Komposit Matriks Aluminium. Prosiding Semnastek.

Triadi, A A Alit., Yudhyadi, I., Suartika, I., & Sari, N. (2019). Efek Suhu Sintering Terhadap Sifat Kekerasan dan Kekuatan Tekan Bahan Campuran Al/Cu/SiC Melalui Proses Metalurgi Serbuk. Dinamika Teknik Mesin, Vol. 9, No. 2, 80-85.

Triadi. AA Alit; Wangi, KGK; Setyawan, PD; (2022), Efek suhu sintering dan komposisi bahan terhadap karakteristik mekanik komposit berbahan limbah aluminium dan kaca menggunakan metode metalurgi serbuk. Jurnal Dinamika Teknik Mesin. 12(1) 19-28

Triadi, AAA; Fathoni MD; Pandiatmi P, (2022), Efek waktu tahan sintering dan komposisi bahan terhadap kekerasan dan struktur makro produk metalurgi serbuk, Jurnal Energy, Material and Product Design. 1(2) 39-45

Yadav, A. K., Pandey, K. M., & Dey, A. (2018). Aluminium Metal Matrix Composite With Straw Ash As Reinforcement: A Review. Materials Today: Proceedings, 5(9), 20130-20137




DOI: https://doi.org/10.35327/gara.v18i3.981

Refbacks

  • There are currently no refbacks.


Copyright (c) 2024 GANEC SWARA

Creative Commons License
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.

https://similarplay.com/